PA66 美國杜邦 ST801 增韌級
| 物理性能 | 測試條件 | 測試方法 | 測試結果 | 單位 |
|---|---|---|---|---|
| 收縮率 | 橫向流量 | ISO 294-4 | 1.4 | % |
| 流量 | ISO 294-4 | 1.8 | % | |
| 吸水率 | 24 hr, 23°C | ISO 62 | 1.1 | % |
| 飽和, 23°C, 2.00 mm | ISO 62 | 6.5 | % | |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.0 | % | |
| 粘數 | ISO 307 | 130 | cm3/g | |
| 機械性能 | 測試條件 | 測試方法 | 測試結果 | 單位 |
| 剪切強度 | ASTM D-732 | DAM｜57.9 | Mpa | |
| ASTM D-732 | 50%RH｜- | Mpa | ||
| 拉伸模量 | ISO 527-2 | 2000 | Mpa | |
| 拉伸強度 | ASTN D-638 | DAM｜517 | Mpa | |
| ASTN D-638 | 50%RH｜41.1 | Mpa | ||
| 拉伸蠕變模量 | 1 hr | ISO 899-1 | -- | Mpa |
| 1000 hr | ISO 899-1 | -- | Mpa | |
| 拉伸應變 | 斷裂 | ISO 527-2 | > 50 | % |
| 拉伸應力 | 50% 應變 | ISO 527-2 | 49.0 | Mpa |
| 撓曲強度 | ASTM D-790 | 50%RH｜862 | Mpa | |
| ASTM D-790 | DAM｜1689 | Mpa | ||
| 伸長率 | 斷裂 | ASTM D-638 | DAM｜80 | % |
| 斷裂 | ASTM D-638 | 50%RH｜210 | % | |
| 彎曲模量 | ISO 178 | 1800 | Mpa | |
| 硬度計硬度 | ASTM D-676 | DAM｜6.7 | ||
| ASTM D-676 | 50%RH｜- | |||
| IZOD沖擊強度 | ASTM D-256 | 50%RH｜1068 | J/m | |
| ASTM D-1822 | DAM｜588 | kJ/m2 | ||
| ASTM D-1822 | 50%RH｜1155 | kJ/m2 | ||
| ASTM D-256 | DAM｜907 | J/m | ||
| 熱性能 | 測試條件 | 測試方法 | 測試結果 | 單位 |
| UL燃燒性 | UL 94 | DAM｜HB | ||
| UL 94 | 50%RH｜HB | |||
| 玻璃轉化溫度 2 | ISO 11357-2 | 75.0 | °C | |
| 熱變形溫度 | 0.45 MPa, 未退火 | ISO 75-2/B | 157 | °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 63.0 | °C | |
| 0.5×106Pa | DAM｜216 | ℃ | ||
| 0.5×106Pa | 50%RH｜- | ℃ | ||
| 18×106Pa | ASTM D-648 | DAM｜71 | ℃ | |
| 18×106Pa | ASTM D-648 | 50%RH｜- | ℃ | |
| 熔點 | ASTM D-789 | DAM｜255 | ℃ | |
| ASTM D-789 | 50%RH｜255 | ℃ | ||
| 熔融溫度 2 | ISO 11357-3 | 262 | °C | |
| 維卡軟化溫度 | ISO 306/B50 | 205 | °C | |
| 線形熱膨脹系數 | 流動 : 23 到 55°C | ASTM E831 | 1.4E-4 | cm/cm/°C |
| 流動 | ISO 11359-2 | 1.4E-4 | cm/cm/°C | |
| 流動 : -40 到 23°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| 流動 : 55 到 160°C | ISO 11359-2 | 1.6E-4 | cm/cm/°C | |
| 橫向 : 23 到 55°C | ASTM E831 | 1.3E-4 | cm/cm/°C | |
| 橫向 | ISO 11359-2 | 1.3E-4 | cm/cm/°C | |
| 橫向 : -40 到 23°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| 橫向 : 55 到 160°C | ISO 11359-2 | 1.3E-4 | cm/cm/°C | |
| 電氣性能 | 測試條件 | 測試方法 | 測試結果 | 單位 |
| 表面電阻率 | IEC 62631-3-2 | -- | ohms | |
| 耗散因數 | 100 Hz | IEC 62631-2-1 | 5.0E-3 | |
| 1 MHz | IEC 62631-2-1 | 0.010 | ||
| 介電常數 | 106Hz | ASTM D-150 | DAM｜2.9 | |
| 106Hz | ASTM D-150 | 50%RH｜3.2 | ||
| 1000Hz | ASTM D-150 | DAM｜3.2 | ||
| 1000Hz | ASTM D-150 | 50%RH｜5.5 | ||
| 108Hz | ASTM D-150 | DAM｜3.2 | ||
| 108Hz | ASTM D-150 | 50%RH｜4.5 | ||
| 介電強度 | IEC 60243-1 | 25 | KV/mm | |
| 漏電起痕指數 | IEC 60112 | 600 | V | |
| 損耗因數 | 106Hz | ASTM D-150 | DAM｜0.02 | |
| 106Hz | ASTM D-150 | 50%RH｜0.03 | ||
| 108Hz | ASTM D-150 | DAM｜0.01 | ||
| 108Hz | ASTM D-150 | 50%RH｜0.01 | ||
| 100Hz | ASTM D-150 | DAM｜0.01 | ||
| 100Hz | ASTM D-150 | 50%RH｜0.02 | ||
| 體積電阻率 | IEC 62631-3-1 | > 1.0E+13 | ohms·m | |
| ASTM D-257 | DAM｜1014 | Ω.m | ||
| ASTM D-257 | 50%RH｜1013 | Ω.m | ||
| 相對電容率 | 1 MHz | IEC 62631-2-1 | 3.30 | |
| 100 Hz | IEC 62631-2-1 | 3.50 | ||
| 沖擊性能 | 測試條件 | 測試方法 | 測試結果 | 單位 |
| 簡支梁無缺口沖擊強度 | 23°C | ISO 179/1eU | -- | |
| 充模分析 | 測試條件 | 測試方法 | 測試結果 | 單位 |
| 頂出溫度 | 190 | °C | ||
| 注射 | 測試條件 | 測試方法 | 測試結果 | 單位 |
| Hold Pressure Time | 4.00 | s/mm | ||
| Maximum Screw Tangential Speed | 18 | m/min | ||
| Melt Temperature, Optimum | 290 | °C | ||
| Mold Temperature, Optimum | 80 | °C | ||
| 保壓 | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| 干燥時間 - 熱風干燥機 | 2.0 到 4.0 | hr | ||
| 干燥溫度 | 80 | °C | ||
| 加工（熔體）溫度 | 280 到 300 | °C | ||
| 建議的水分含量 | 0.20 | % | ||
| 模具溫度 | 50 到 100 | °C | ||
| 可燃性 | 測試條件 | 測試方法 | 測試結果 | 單位 |
| FMVSS 可燃性 | FMVSS 302 | B | ||
| UL 阻燃等級 | 0.8 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | ||
| 極限氧指數 | ISO 4589-2 | 20 | % | |
| 燃燒速率 | 1.00 mm | ISO 3795 | < 100 | mm/min |
| 基本性能 | 測試條件 | 測試方法 | 測試結果 | 單位 |
| 吸水率 | 飽和 | ASTM D-570 | DAM｜6.7 | % |
| 飽和 | ASTM D-570 | 50%RH｜- | % | |
| 24hr | ASTM D-570 | DAM｜1.2 | % | |
| 24hr | ASTM D-570 | 50%RH｜- | % | |
| 需氧指數 | ASTM D-2863 | DAM｜15 | % | |
| ASTM D-2863 | 50%RH｜19 | % |