本水性產品采用水性樹脂、顏料、助劑經過特殊工藝加工而成。產品內不含甲醛及二甲苯類有毒物質，以凈水作為稀釋劑，環(huán)保安全防火，不燃不爆。產品對玻璃具有優(yōu)異的附著性能和光學透明性，不僅同時具有高硬度，與溶劑型玻璃烘烤相比，耐老化性能好，無毒、無污染、不易爆，施工簡便。
This aquatic product is made of imported pure water resin, high grade pigment and auxiliary agent. The product does not contain formaldehyde and xylene toxic substances, with water as a diluent, environmental protection, safety, fire, no explosion. Products on the glass with excellent adhesion and optical transparency, not only at the same time with a high hardness, compared with the solvent based glass baking, anti-aging performance is good, non-toxic, non polluting, non explosive, construction is simple.
適用范圍：
適用于各種鍍鋁、銀、銅、酒瓶、化妝瓶等玻璃器具表面涂裝。
Scope of application：
For a variety of aluminum plating, silver, copper, wine bottle, cosmetic bottles and glassware surface coating.
施工配比：
按照漆液：凈水=100：20-30稀釋，攪拌均勻后用400目濾布過濾，靜置消泡即可使用。
Construction proportion:
in accordance with the liquid paint: pure water =100:20-30 dilution, mixing evenly with 400 mesh filter cloth filter, static defoaming can be used.
產品優(yōu)勢：
1、省漆：低粘高固，涂布率高，揮發(fā)消耗少。
2、噴涂霧化性好。
3、烘烤溫度寬容性強，烘烤溫度120-150℃，烘烤時間在10-30min內進行調節(jié)。
4、八大重金屬、多環(huán)芳烴和雙酚A符合歐盟標準。
5、耐水煮性能佳，較高可達到72小時。
6、通過洗碗機測試。
7、優(yōu)異的附著力與抗沖擊強度，漆膜豐滿滑爽，保光性優(yōu)。
Product advantages:
1, the provincial paint: low viscosity high solid coating rate, consume less volatile.
2, good spray atomization.
3, the baking temperature tolerance strong, baking temperature 120-150℃, baking time is adjusted within a 10-30min.
4, eight heavy metals, polycyclic aromatic hydrocarbons and bisphenol A in line with EU standards.
5, excellent resistance to boiling performance, up to 72 hours.
6, through the dishwasher test.
7, excellent adhesion and impact strength, smooth paint film, gloss retention excellent.
技術指標：
烘烤溫度： 180℃/30min
粘度（涂2杯，S/25℃）： 25-30
PH值： 7.5-8
硬度： 2H-3H
附著力： 0級
固含量： 40-55
耐水性： ＞240h，不起泡，不脫落
耐鹽霧： ＞240 h，不起泡，不脫落
耐酒精： ＞24 h，不起泡，不脫落
Technical indicators:
Baking temperature:180℃/ 30min
Viscosity (Tu 2 cups, S / 25℃):25-30
PH:7.5-8
Hardness:2H-3H
Adhesion:0 level
Solid content:40-55
Water resistance: