GGT-RSC High Temp Nonmetallic Thread Compound for Rotary-Shouldered Connections NSF Registered COLOR Black PENETRATION 300 - 320 (ASTM D 217) WEIGHT/GALLON 10.7 pounds/gallon DROPPING POINT 500º F/260º C (typ) FLASH POINT 385º F/196º C (min) BRUSHABLE TO 15º F/-9º C SERVICE RATING 600º F/316º C TORQUE FACTOR 1.0 (per API RP 7A1)* CONTAINS Synthetic and amorphous graphite, and other nonmetallic additives GGT-RSC High Temp has been developed as an economical answer to the environmental restrictions and exposure concerns associated with the use of drilling compounds that contain heavy metals, such as lead and zinc. It contains a high percentage of amorphous and synthetic graphites, as well as other inert solids, in a high temperature base grease. In addition to the galling and seizing protection provided by the solids, GGT-RSC High Temp also contains a soluble extreme pressure package that is surface active (adheres to metal surfaces) and helps to provide the load-carrying capability required by the high-bearing stresses present in rotary-shouldered connections. It applies easily in a wide range of temperatures and conditions, is resistant to wash-out, and will not harden or bleed excessively in storage. It is recommended for light-to-medium duty drilling. GGT-RSC HT has obtained registration from NSF, National Sanitation Foundation. *API RP 7A1: “Recommended Practice for Testing of Thread Compound for Rotary Shouldered Connections” NOTE: Due to operation and equipment variables, this value may require adjustment based on field experience. DO NOT USE ON OXYGEN LINES OR IN OXYGEN ENRICHED ATMOSPHERES.